STP® Global Extended Life Antifreeze/Coolant
STP® Global Extended Life Antifreeze/Coolant is recommended for use in all makes and models of foreign and domestic passenger vehicles and light duty trucks. It contains a proprietary formulation of premium corrosion inhibitors that provide extended protection against rust, corrosion and pitting caused by cavitation for all coolant system metals. It also provides excellent protection against temperature extremes, preventing freeze-up and boil over when used in accordance with OEM and product manufacturer’s guidelines regarding product dilution.
This product does not impart any colour change if mixed with another engine coolant. The superior performance and stability of premium extended life corrosion inhibitors allows them to go on working well beyond the lifetime of traditional products. When STP® Global Extended Life Antifreeze/Coolant is added to a coolant system after a complete drain, flush and fill, this product provides up to 250,000 km or 5 years of protection.
STP® Global Extended Life Antifreeze/Coolant offers the following advantages:
- Recommended for use in all makes and models of foreign and domestic passenger vehicles and light duty trucks
- Add as top-up to any colour antifreeze
- Protects coolant system metals such as brass, copper, solder, steel, cast iron and aluminum
- Guarantee: Up to 5 years or 250,000 km protection whichever comes first when added as initial fill or when added to a well maintained, clean coolant system after a complete drain, flush and fill
STP® Global Extended Life Antifreeze/Coolant meets the performance requirements of the following specifications:
- ASTM D-3306
- JIS K-2234
Coolant concentrate must be diluted with water prior to use. STP® Global Extended Life Antifreeze/Coolant should not be used in concentrated form. A 50% dilution is generally recommended for the best balance of protection against freezing, corrosion and summer boil-over. For increased freeze protection in extremely cold areas, a 60% volume concentration can be used. Concentrations of greater than 70% by volume are not recommended. High quality soft, de-ionized or distilled water should always be used to dilute coolant concentrate.
3.78 L/ 4
Typical Product Properties
|pHa||7.5 – 8.6||ASTM D1287|
|Specific gravityb||1.120 – 1.140||ASTM D1122|
|Freeze pointa, °C/°F||-37/ -34||ASTM D1177|
|Foam volume, ml||150 max.||ASTM D1881|
|Foam break time, second||5 max.||ASTM D1881|
|Reserve Alkalinity, ml||3.0 min.||ASTM D1121|
|Chloride, ppm||25 max.||ASTM D3634|
|Glycol Content (wgt.%).||93 min.|
|Inhibitors and Water Content (wgt.%)||7.0 max.|
|Silicon (ppm)||< 10||ASTM D6130|
|Boron (ppm)||< 10|
|Phosphorous (ppm)||< 10|
a 50% volume aqueous solution
b Measured at 15.6ºC/60ºF
Typical Coolant Performance Testing Results
|Metal Type||ASTM D 1384 GLASSWARE CORROSION||ASTM D 2570 SIMULATED SERVICE|
|Test Results¹||Max. Spec.||Test Results¹||Max. Spec.|
1 Weight loss, except negative sign which indicate weight gain, per coupon in milligrams. Values are for coolant made from virgin ethylene glycol.
|ASTM D4340 Heat Rejecting Aluminum Corrosion (mg/cm²/week)||0.1||1.0 maximum|
|ASTM D2809 Aluminum Water Pump Cavitation- Erosion Corrosion Rating||9||8 minimum|
1 Weight loss per coupon in milligrams (average for 2 tests). Values are for coolant made from virgin ethylene glycol.